ASTM STANDARD 10B21 Cold Heading Quality Wire Rod Corrosion Resistant
Wire Rod (W/R)
Wire rod is a rolled alloy or non-alloy steel product, produced from a semi (e.g. bloom) and having a round, rectangular, hexagon, octagon, semicircle or other cross-section. Particularly fine cross-sections may be achieved by subsequent cold forming (drawing). Wire rod is wound into coils and transported in this form.
SWRCH18A and SWRCH22A belong to the surface hardening steel for cold heading and cold extruding, which are mainly used to produce dry wall screw, self tapping screw, single nail, wood screw, chipboard screw, fast screw furniture nail, flat self drilling screw, pan self drilling screw, round self drilling screw, hex flange self drilling screw, etc.
It adopts the standard of JIS G 3507 for the carbon steel wire rod of cold heading. The chemical compositions are as follows:
|Grade||Chemical Compositions (%)|
The grades SWRCH18A and SWRCH22A are ML18Mn and ML22Mn in GB/T 6478-2001 respectively.
The wire rod is delivered on hot rolled status.
There must be no cracks in the cold heading test. The height rate of after and before cold heading is 1/2.
The others should be implemented accroding to GB/T 6478-2001.
The main diameters are 5.5mm and 6.5mm.
Adopting the American Standard and with no equivalent grade in China, we have the ability to produce 5.5~16mm, among which, 5.5mm is the main rolling product at present.
With better plasticity, cold heading performances and better hardenability, 10B21 produced by our company can omit the spheroidizingannealing treatment for the medium carbon bolt.
|Features||With the advantages as stable contents, low harmful elements, high steel purity, less decarburizing depth, less surface defect, low original hardness of the wire rod, etc. 10B21 is mainly used to produce the standard pieces of property elasses 8.8~10.9 and it is worth spreading for such performances as being directly manufactured without annealing process, low cracking rate when cold heading and good hardenability.|
|Application||It is applicable to manufacture fasteners of property elasses 8.8~10.9 and various specifications and the components of common use.|
|Future Developments||Through reasonable alloys additions and controlled cooling process, it can keep the hot rolled wire rod in lower hardness for the convenience of being cold heading without spheroidizing annealing treatment and can reach higher strength after heat treatment.|
The chemical compositions are as follows:
|Grade||Chemical Compositions (%)|
Available Chinese Mills:
Xingtai, WISCO, Capital steel, NISCO, Pingxiang, Shaoguan, Baotou, Xiangtan, Shagang, Hangzhou, Maanshan, Jiuquan, Jiujiang,,Antai,Tianzhu,Beitai,Etc and some other medium/small mills
Packaging & Delivery
Packaging Details: inner plastic film, outside plastic bags, 10kg/roll, 20kg/roll,25kg/roll,50kg/roll,100kg/roll
Delivery Detail: within 12 days
Who can be our (sole)agent:
With good experience in steel biz,good connections with various endbuyers in the country,to be powerful in developing new customers.
The agent should collect market information including prices and demands and report to Fortune Best regularly to analyze market demand,shall develop new customer and bring new business to us.
Agent protection policy:
Any client brought by the agent will be channelized through this agent in reasonable period. If you are chosen to be our sole agent in your country/area,all the orders related to your territory shall share margin with you.
Daily business running is on its own cost. We don’t pay agent monthly fee or salary. Agent will enjoy min.30% of total pure margin (pure margin means total margin deduct financial charges), which is to be paid within 7 days after Fortune Best receiving payment from clients.
Contact Person: Yuli